CoolplusⅡ® 为模仿自然生态并赋予纤维表面无数微細长孔高科技纤维。CoolplusⅡ®织物使肌肤感受到前所未有的清爽,可过到许多传统织物梦寐以求的特性。
Coolplus Ⅱ is a completely new fiber with distinguished-looking texture.A number of micro-slits distributed on the fiber surface impart CoolplusII to have natural characteristics of rayon and silk.
其突出优点:
▲深色浓染效果
deep brilliant color
▲优雅的悬垂性
elegant drape
▲质轻,粘胶纤维般的柔軟
light weight and execellent sensitivity
▲ 干爽
dry touch
▲吸湿排汗
water transport
CoolplusⅡ性能介绍
1、 CoolplusⅡ的浓染效果
CoolplusⅡ®具有浓染效果的原理
CoolplusⅡ®表面之凹凸狹縫构造，使光产生乱反射，而大部分被纤维內部吸收，結果使得顏色之深色性大增，提高鮮明度而具有浓染效果.
Coolplus Ⅱ has porous surface which suppress light reflection at the fiber surface therefore the fiber isa able to exhibit brilliant black which conventional fibers can not achieve.
下圖為光照射到CoolplusII产生乱反射的情形
2、 CoolplusⅡ之吸湿排汗特性
CoolplusⅡ®为何具有良好吸湿排汗效果
CoolplusⅡ®為利用材料溶解性差异，赋予纤维无数微细孔洞的新机能性纤维，具有吸湿排汗功能.经由纤维表面的细长孔洞产生毛細現象，将肌肤表层排出的湿气与汗水经由芯吸，扩散，传输的作用，瞬间排出体外.而使肌肤保持干爽与涼快。
CoolplusII is a new fiber that features water diffusion and wicking properties via innumerable micro slit on fiber surface.
As a result the fabric does not stick to the skin and shows cool crispy wearing comfortable due to its capillary action. In addition,the dry touch can be maintained even it is wet.
下图为CoolplusII与其他纤维干燥扩散能力比較
3、 CoolplusⅡ之低起毛球特性
CoolplusⅡ®所具有低起毛球能力
CoolplusⅡ®精练后損失大部分重量，纤维强力随重量損失率增加而下降，使织物在精练加工后具有低起毛球特性。
Coolplus Ⅱ will loss some weight after refining.
Tenacity loss is proportional to weight loss percent. Therefore fabric reaches different anti-pilling grade by control of refuning time and temperature.
下图为CoolplusII重量損失率与纤维强力关系
4、CoolplusⅡ精练条件
CoolplusⅡ®精練條件:
碱浓度: 5~7 g/l NaOH(片碱)
精练温度: 110~120 °C
精练时间: 30min
精练后pilling等級3級
注意事項:
- 因织物精练后損失部分重量，布匹组织密度需较高，以免精练后过于松散
- 不可使用Silicone系列柔软剂
Suggested refining conditions:
Alkali concentration 5~7 g/l (NaOH solid) x 110~120 °C x 30 min
Pilling grade 3 after refining
Note:
-Fabric is getting loose after refining ,
so to preset a higher fabric density is required for compensation.
-Do not use silicon softener.
5、CoolplusⅡ详细規格
联系方式：台湾中兴纺织集团
|